NSF Certified Certified to ANSI/NSF Standard 61 for use in commercial and residential potable water systems not exceeding 82° C.
UL Classification Classified as small fire hazard. No flash point in liquid state. Ignition temperature 465°C. For use in devices handling gasoline, petroleum oils, natural gas, propane and butane.
Pressure Resistance TURBO SEAL SERIES 80 was successfully tested for pressure resistance and sealability to 3,000 psi 3/8” NPT steel pipe tees and plugs were assembled and pre-torqued to 27 N.m and allowed to cure 24 hours prior to testing at 3,000 psi hydraulic pressure according to ASTM D 1599.
Part Numbers for this data: 80-051, 80-251, 80-300, 80-1000, 80-2000
Information provided by Palm Laboratories Adhesives| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | |
| 布氏粘度 | cP | cP | RVT Spindle 3 @ 20 rpm |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 剪切强度 | >= MPa | >= psi | Steel Pins & Collars; ISO 10123 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | ASTM D696 |
| 比热容 | J/g-°C | BTU/lb-°F | |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C177 |
| Flash Point | >= °C | >= °F |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 固化时间 | min | hour | Functional |
| min | hour | Full | |
| min @Temperature -65.0 - 300 °C | hour @Temperature -85.0 - 572 °F | Handling |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | White | |
| 耐化学性 | 100% Initial Strength Retained | Motor Oil at 125°C, at 500hrs |
| 100% Initial Strength Retained | Gasoline at 22°C, at 500hrs | |
| 100% Initial Strength Retained | Brake Fluid at 22°C, at 500hrs | |
| 100% Initial Strength Retained | Water/Glycol at 87°C, at 500hrs | |
| 85% Initial Strength Retained | Acetone at 22°C, at 1000hrs | |
| 90% Initial Strength Retained | Ethanol at 22°C, at 1000hrs | |
| 90% Initial Strength Retained | Acetone at 22°C, at 500hrs | |
| 90% Initial Strength Retained | Ethanol at 22°C, at 500hrs | |
| 90% Initial Strength Retained | Water/Glycol at 87°C, at 1000hrs | |
| 95% Initial Strength Retained | Motor Oil at 125°C, at 1000hrs | |
| 95% Initial Strength Retained | Gasoline at 22°C, at 1000hrs | |
| 95% Initial Strength Retained | Brake Fluid at 22°C, at 1000hrs | |
| 组成 | Methacrylate ester | |
| Torque | >2.8 N.m | Breakaway, M10 steel nuts and bolts, ISO 10964 |
| 1 N.m | Prevail, M10 steel nuts and bolts, ISO 10964 |