ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin物性表-搜物性

Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.

Information provided by ExxonMobil Chemical

搜物性提供30万余种物性表数据，如要查看关于 ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin 完整物性数据，以及其替代物，黄卡信息，下载物性表PDF.

请获得完整功能体验。

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	ExxonMobil Method
Vinyl Acetate Content			ExxonMobil Method
熔体流动速率	g/10 min	g/10 min	ASTM D1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(MD : 屈服)	MPa	psi	at 2% offset; ASTM D882
抗张强度(TD : 屈服)	MPa	psi	at 2% offset; ASTM D882
断裂伸长率，MD			ASTM D882
断裂伸长率，TD			ASTM D882
Film Elongation at Yield, MD			ASTM D882
Film Elongation at Yield, TD			ASTM D882
埃尔曼多夫抗撕强度(MD)	g/micron	g/mil	ASTM D1922
埃尔曼多夫抗撕强度(TD)	g/micron	g/mil	ASTM D1922
落锤	g/micron	g/mil	ASTM D1709
抗张强度(MD : 断裂)	MPa	psi	ASTM D882
抗张强度(TD : 断裂)	MPa	psi	ASTM D882
割线模量(1% 正割 MD)	MPa	psi	ASTM D882
割线模量(1% 正割 TD)	MPa	psi	ASTM D882

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	°C	°F	Peak Melting Temperature; ExxonMobil Method
维卡软化温度	°C	°F	ASTM D1525

光学性能	额定值 (公制)	额定值 (英制)	测试方法
雾度			ASTM D1003
光泽度			45°; ASTM D2457

材料描述		测试方法
特性	Thermal Stabilizer

此数据表中的信息由搜聚从该材料的生产商处获得。搜聚尽最大努力确保此数据的准确性。但是搜聚对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。

ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin