| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc @Temperature 25.0 °C | lb/in³ @Temperature 77.0 °F | Liquid |
| 粘度 | cP @Temperature 30.0 °C | cP @Temperature 86.0 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 90 Minute UV Cure; ASTM D2240 | ||
| 90 Minute UV Cure + Thermal; ASTM D2240 | |||
| 抗张强度(屈服) | MPa | psi | 90 Minute UV Cure; ASTM D638 |
| MPa | psi | 90 Minute UV Cure + Thermal; ASTM D638 | |
| 伸长率 (断裂) | 90 Minute UV Cure; ASTM D638 | ||
| 90 Minute UV Cure + Thermal; ASTM D638 | |||
| 拉伸模量 | GPa | ksi | 90 Minute UV Cure; ASTM D638 |
| GPa | ksi | 90 Minute UV Cure + Thermal; ASTM D638 | |
| 弯曲强度 | MPa | psi | 90 Minute UV Cure; ASTM D790 |
| MPa | psi | 90 Minute UV Cure + Thermal; ASTM D790 | |
| 弯曲模量 | GPa | ksi | 90 Minute UV Cure + Thermal; ASTM D790 |
| GPa | ksi | 90 Minute UV Cure; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | 90 Minute UV Cure; ASTM D256 |
| J/cm | ft-lb/in | 90 Minute UV Cure + Thermal; ASTM D256 | |
| Penetration | mils |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | 90 Minute UV Cure + Thermal; T<Tg; ASTM E831-93 |
| µm/m-°C | µin/in-°F | 90 Minute UV Cure; T<Tg; ASTM E831-93 | |
| µm/m-°C | µin/in-°F | 90 Minute UV Cure + Thermal; T>Tg; ASTM E831-93 | |
| µm/m-°C | µin/in-°F | 90 Minute UV Cure; T>Tg; ASTM E831-93 | |
| 载荷下热变形温度(0.46 MPa) | °C | °F | 90 Minute UV Cure; ASTM D648 |
| °C | °F | 90 Minute UV Cure + Thermal; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | 90 Minute UV Cure; ASTM D648 |
| °C | °F | 90 Minute UV Cure + Thermal; ASTM D648 | |
| 玻璃化转变温度，Tg | °C | °F | 90 Minute UV Cure; DMA, E" |
| °C | °F | 90 Minute UV Cure + Thermal; DMA, E" |
| 材料描述 | 测试方法 | |
|---|---|---|
| 外观 | Clear amber | |
| Critical Exposure (mJ/cm²) | 13.9 | |
| Tested Build Styles | EXACT™ |