Overview of materials for Nylon 6, Cast

This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Cast". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	Average value: 1.14 g/cc Grade Count:63
吸水率			Average value: 1.37 % Grade Count:28
平衡吸湿			Average value: 2.05 % Grade Count:33
饱和吸水率			Average value: 5.75 % Grade Count:48

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（M 级）			Average value: 84.9 Grade Count:16
洛氏硬度（R 级）			Average value: 113 Grade Count:22
肖氏硬度 (邵氏 D)			Average value: 80.2 Grade Count:28
球压硬度	MPa	psi	Average value: 140 MPa Grade Count:35
极限抗拉强度	MPa	psi	Average value: 75.5 MPa Grade Count:38
抗张强度(屈服)	MPa	psi	Average value: 70.8 MPa Grade Count:27
伸长率 (断裂)			Average value: 36.4 % Grade Count:49
屈服伸长率			Average value: 5.00 % Grade Count:5
Creep Strength	MPa	psi	Average value: 15.6 MPa Grade Count:15
弹性模量	GPa	ksi	Average value: 2.96 GPa Grade Count:64
	GPa @Temperature 100 - 100 °C	ksi @Temperature 212 - 212 °F	Average value: 0.600 GPa Grade Count:2
弯曲强度	MPa	psi	Average value: 96.3 MPa Grade Count:48
弯曲模量	GPa	ksi	Average value: 2.81 GPa Grade Count:45
压缩屈服强度	MPa	psi	Average value: 66.0 MPa Grade Count:42
压缩模量	GPa	ksi	Average value: 2.28 GPa Grade Count:20
剪切强度	MPa	psi	Average value: 66.3 MPa Grade Count:15
悬壁梁缺口冲击强度	J/cm	ft-lb/in	Average value: 0.484 J/cm Grade Count:22
	kJ/m²	ft-lb/in²	Average value: 11.1 kJ/m² Grade Count:19
简支梁无缺口冲击强度	J/cm² - NB	ft-lb/in² - NB	Average value: 5.63 J/cm² Grade Count:18
简支梁缺口冲击强度	J/cm²	ft-lb/in²	Average value: 1.24 J/cm² Grade Count:20
拉伸冲击强度	kJ/m²	ft-lb/in²	Average value: 72.0 kJ/m² Grade Count:3
摩擦系数			Average value: 0.233 Grade Count:49
静态摩擦系数			Average value: 0.240 Grade Count:5
撕裂强度测试			Average value: 0.375 Grade Count:14
K Factor (Wear Factor)			Average value: 7.67e-11 Grade Count:12
K (wear) Factor	x 10-8 mm³/N-M	x 10-10 in³-min/ft-lb-hr	Average value: 203 x 10<sup>-8</sup> mm³/N-M Grade Count:12
Limiting Pressure Velocity	MPa-m/sec	psi-ft/min	Average value: 0.412 MPa-m/sec Grade Count:12

电气性能	额定值 (公制)	额定值 (英制)	测试方法
电阻率	ohm-cm	ohm-cm	Average value: 3.61e+14 ohm-cm Grade Count:39
表面电阻	ohm	ohm	Average value: 4.31e+12 ohm Grade Count:35
介电常数			Average value: 3.94 Grade Count:51
介电强度	kV/mm	kV/in	Average value: 27.8 kV/mm Grade Count:48
耗散因数			Average value: 0.0239 Grade Count:16
介电损耗指数			Average value: 0.0318 Grade Count:17
相比耐漏电起痕指数(CTI)	V	V	Average value: 600 V Grade Count:12

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	µm/m-°C	µin/in-°F	Average value: 81.9 µm/m-°C Grade Count:62
比热容	J/g-°C	BTU/lb-°F	Average value: 1.67 J/g-°C Grade Count:17
导热系数	W/m-K	BTU-in/hr-ft²-°F	Average value: 0.260 W/m-K Grade Count:41
熔融温度	°C	°F	Average value: 219 °C Grade Count:60
最高工作温度, Air	°C	°F	Average value: 131 °C Grade Count:61
载荷下热变形温度(0.46 MPa)	°C	°F	Average value: 203 °C Grade Count:30
载荷下热变形温度(1.8 MPa)	°C	°F	Average value: 117 °C Grade Count:45
最低工作温度, Air	°C	°F	Average value: -45.1 °C Grade Count:34
玻璃化转变温度，Tg	°C	°F	Average value: 39.2 °C Grade Count:5
可燃性(UL94)			Grade Count:32
极限氧指数			Average value: 25.0 % Grade Count:6