Processing: Injection and compression molding
Applications: Molded parts in electrical engineering, mainly electrical parts such as circuit breakers, relays, switches, contact terminals.
Information provided by the Raschig Group
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ISO 1183 |
| 表观密度 | g/cc | lb/in³ | ISO 60 |
| 吸水率 | @Temperature 23.0 °C, Time 86400 sec | @Temperature 73.4 °F, Time 24.0 hour | ISO 62 |
| 线性成型收缩率 | cm/cm | in/in | Injection and Compression; ISO 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | Compression; ISO 527 |
| MPa | psi | Injection; ISO 527 | |
| 弹性模量 | GPa | ksi | Compression; ISO 527 |
| GPa | ksi | Injection; ISO 527 | |
| 弯曲强度 | MPa | psi | Compression; ISO 178 |
| MPa | psi | Injection; ISO 178 | |
| 弯曲模量 | GPa | ksi | Compression; ISO 178 |
| GPa | ksi | Injection; ISO 178 | |
| 抗压强度 | MPa | psi | ISO 604 |
| 简支梁无缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Compression; ISO 179/ 1eU |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Injection; ISO 179/ 1eU | |
| 简支梁缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Compression; ISO 179/ 1eA |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Injection; ISO 179/ 1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | IEC 60093 |
| 表面电阻 | ohm | ohm | IEC 60093 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 100 Hz | @Frequency 100 Hz | IEC 60250 | |
| 介电强度 | kV/mm | kV/in | IEC 60243-1 |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 100 Hz | @Frequency 100 Hz | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | V | V | CTI; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature 50.0 - 100 °C | µin/in-°F @Temperature 122 - 212 °F | ISO 11359-2 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM E1461 |
| 最高工作温度, Air | °C | °F | 20,000 h; IEC 216/T1 |
| °C | °F | < 50 h; IEC 216/T1 | |
| 载荷下热变形温度(1.8 MPa) | >= °C | >= °F | ISO 75-A |
| 载荷下热变形温度(8.0 MPa) | °C | °F | ISO 75-C |
| 可燃性(UL94) | @Thickness 0.750 mm | @Thickness 0.0295 in | |
| 流量 | @Temperature 110 °C, Time 605000 sec | @Temperature 230 °F, Time 168 hour | Post shrinkage; ISO 2577 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 保质期 | Month @Temperature 15.0 - 25.0 °C | Month @Temperature 59.0 - 77.0 °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| Arc Resistance | 4 Stufe | ASTM D495 |
| Glow wire ignitability test | 825/1 | IEC 60695 2-13 |
| Glow-wire flammability test | 960/1 | IEC 60695 2-12 |
| Water Absorption | <50 mg | ISO 62; 24h / 23°C |