Denka TX-400S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene

"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a good balance of transparency, strength and fluidity (methyl methacrylate butadiene styrene), "TE Series/CL Series," transparent ABS resins with excellent color attributes and tensile strength are available (among others).

Applications

TX is used for:

• flat display substrates
• optical components
• miscellaneous goods.

TP/TH are used for:

• food package sheeting as well as in manufacturing
• electronic equipment and components
• miscellaneous goods

TE/CL are for:

• electronic equipment and components
• information equipment components
• AV equipment, etc.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	ASTM D792
密度	g/cc	lb/in³	ISO 1183
熔体流动速率	g/10 min @Load 5.00 kg, Temperature 200 °C	g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
	g/10 min @Load 10.0 kg, Temperature 220 °C	g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（M 级）			ISO 2039-2
抗张强度(断裂)	MPa	psi	5mm/min; ASTM D638
	MPa	psi	5mm/min; ISO 527-2
伸长率 (断裂)			5mm/min; ISO 527-2
弯曲强度	MPa	psi	2mm/min; ASTM D790
	MPa	psi	ISO 178
弯曲模量	GPa	ksi	2mm/min; ISO 178
	GPa	ksi	2mm/min; ASTM D790
Izod Impact Resistance	J/cm²	ft-lb/in²
简支梁缺口冲击强度	J/cm²	ft-lb/in²	ISO 179-2

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(1.8 MPa)	°C	°F	ISO 75-2
	°C	°F	ASTM D648
维卡软化温度	°C	°F	50N; ISO 306
可燃性(UL94)

光学性能	额定值 (公制)	额定值 (英制)	测试方法
雾度	@Thickness 2.00 mm	@Thickness 0.0787 in	ISO 14782
Transmission, Visible	@Thickness 2.00 mm	@Thickness 0.0787 in	ISO 13468-1