Thermal Ceramics Kaolite 2600-LI Insulation Castables

Kaolite 2600-LI is designed specifically for use in petrochemical applications. It incorporates a cement of sufficient purity for low iron content and high-intermediate temperature strengths.

Features:

Light weight and low thermal conductivity reduce both the quantity of heat storage and heat transfer producing significant savings in furnace fuel consumption

Lower densities reduce the amount of supporting furnace steelwork required and provide more insulation with a thinner lining.

Applications:

Backup insulation in two component linings in petrochemical process units

Hot face lining in ductwork from waste heat recovery boilers and process unit

F.C.C.U. linings - regenerator.

Hydrogen or reducing atmosphere linings

Radiant section in steam flood generators.

Hydrogen or reducing atmosphere linings.

Steam flood generator convection sections and target walls

Cat cracker regenerator linings

Petrochemical applications

Information provided by Thermal Ceramics

Data has not been recently verified. Please contact manufacturer for current information.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	Fired at 1500°F
	g/cc	lb/in³	Fired at 2600°F

机械性能	额定值 (公制)	额定值 (英制)	测试方法
断裂模数	GPa	ksi	Dried 18-24 hours at 220°F; ASTM C133
	GPa @Treatment Temp. 816 °C, Time 18000 sec	ksi @Treatment Temp. 1500 °F, Time 5.00 hour	ASTM C133
	GPa @Treatment Temp. 1370 °C, Time 18000 sec	ksi @Treatment Temp. 2500 °F, Time 5.00 hour	ASTM C133
抗压强度	MPa	psi	Fired 5 hours at 1500°F
	MPa	psi	Dried for 18-24 hours at 220°F
	MPa	psi	Fired 5 hours at 2600°F

热性能	额定值 (公制)	额定值 (英制)	测试方法
导热系数	W/m-K @Temperature 260 °C	BTU-in/hr-ft²-°F @Temperature 500 °F	ASTM C417
	W/m-K @Temperature 538 °C	BTU-in/hr-ft²-°F @Temperature 1000 °F	ASTM C417
	W/m-K @Temperature 816 °C	BTU-in/hr-ft²-°F @Temperature 1500 °F	ASTM C417
	W/m-K @Temperature 1090 °C	BTU-in/hr-ft²-°F @Temperature 2000 °F	ASTM C417
最高工作温度, Air	°C	°F
流量			Dried 18-24 hours at 220°F; ASTM C113
	@Temperature 1430 °C, Time 18000 sec	@Temperature 2600 °F, Time 5.00 hour	ASTM C113
	@Temperature 816 °C, Time 18000 sec	@Temperature 1500 °F, Time 5.00 hour	ASTM C113

加工性能	额定值 (公制)	额定值 (英制)	测试方法
保质期	Month	Month

构成要素属性	额定值 (公制)	额定值 (英制)	测试方法
Al2O3
Alkalis
氧化钙
氧化铁
氧化镁
二氧化硅
TiO2