Typical Application Areas: Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.
Information Provided by VICTREX®| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Crystaline; ISO 1183 |
| Water Absorption at Saturation | @Temperature 23.0 °C | @Temperature 73.4 °F | immersion; ISO 62-1 |
| @Temperature 100 °C | @Temperature 212 °F | immersion; ISO 62-1 | |
| 粘度 | cP @Temperature 420 °C | cP @Temperature 788 °F | melt; ISO 11443 |
| 线性成型收缩率,Flow | cm/cm | in/in | 405°C nozzle, 190°C tool; ISO 294-4 |
| 线性成型收缩率，横向 | cm/cm | in/in | 405°C nozzle, 190°C tool; ISO 294-4 |
| Spiral Flow | cm @Thickness 1.00 mm | in @Thickness 0.0394 in | 405°C nozzle, 190°C tool |
| cm @Thickness 3.00 mm | in @Thickness 0.118 in | 405°C nozzle, 190°C tool |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa @Temperature 275 °C | psi @Temperature 527 °F | ISO 527 |
| MPa @Temperature 175 °C | psi @Temperature 347 °F | ISO 527 | |
| MPa @Temperature 125 °C | psi @Temperature 257 °F | ISO 527 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 527 | |
| 伸长率 (断裂) | ISO 527 | ||
| 拉伸模量 | GPa | ksi | ISO 527 |
| 弯曲强度 | MPa @Temperature 275 °C | psi @Temperature 527 °F | ISO 178 |
| MPa @Temperature 175 °C | psi @Temperature 347 °F | ISO 178 | |
| MPa @Temperature 125 °C | psi @Temperature 257 °F | ISO 178 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 178 | |
| 弯曲模量 | GPa | ksi | ISO 178 |
| 抗压强度 | MPa @Temperature 200 °C | psi @Temperature 392 °F | ISO 604 |
| MPa @Temperature 120 °C | psi @Temperature 248 °F | ISO 604 | |
| MPa @Temperature 23.0 °C | psi @Temperature 73.4 °F | ISO 604 | |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180/A |
| 悬壁梁无缺口冲击强度 | kJ/m² | ft-lb/in² | ISO 180/U |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179/1U |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | IEC 60093 |
| 介电常数 | @Frequency 1000 Hz | @Frequency 1000 Hz | IEC 60250 |
| 介电强度 | kV/mm @Thickness 2.00 mm | kV/in @Thickness 0.0787 in | IEC 60243-1 |
| 介电损耗指数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| 相比耐漏电起痕指数(CTI) | V | V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature <=143 °C | µin/in-°F @Temperature <=289 °F | Average below Tg; ASTM D696 |
| µm/m-°C @Temperature >=143 °C | µin/in-°F @Temperature >=289 °F | Average above Tg; ASTM D696 | |
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature <=143 °C | µin/in-°F @Temperature <=289 °F | Below Tg; ASTM D696 |
| µm/m-°C @Temperature >=143 °C | µin/in-°F @Temperature >=289 °F | Above Tg; ASTM D696 | |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | Average; ISO 22007-4 |
| W/m-K | BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 | |
| 熔融温度 | °C | °F | ISO 11357 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75A-f |
| 玻璃化转变温度，Tg | >= °C | >= °F | Onset; ISO 11357 |
| °C | °F | Midpoint; ISO 11357 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | <= °C | <= °F | Hopper Temperature |
| 射嘴温度 | °C | °F | |
| 模具温度 | °C | °F | |
| Dry Time | hour @Temperature 150 °C | hour @Temperature 302 °F | |
| hour @Temperature 120 °C | hour @Temperature 248 °F |