SABIC Innovative Plastics Lexan® FXE1810T PC Copolymer

Polycarbonate (PC)

SABIC Innovative Plastics (GE Plastics)

产品说明

Lexan* FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade. This specialty PC offers excellent processability, very high flow and improved ductility characteristics over standard PC.Lexan FXE1810T resin may be an excellent candidate for a wide variety of applications.This product is available in the Visual fX* Piano Black, Raven Black & Illuminate color range only.

This data was supplied by SABIC-IP for the Americas region.

物理性能额定值 (公制)额定值 (英制)测试方法
比重 g/cc g/cc ASTM D 792
密度 g/cc lb/in³ ISO 1183
平衡吸湿 23°C / 50% RH; ISO 62
饱和吸水率
@Temperature 23.0 °C
@Temperature 73.4 °F
ISO 62
线性成型收缩率,Flow cm/cm
@Thickness 3.20 mm
in/in
@Thickness 0.126 in
SABIC Method
熔体流动速率 g/10 min
@Load 1.20 kg, Temperature 300 °C
g/10 min
@Load 2.65 lb, Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
g/10 min
@Load 1.20 kg, Temperature 300 °C
g/10 min
@Load 2.65 lb, Temperature 572 °F
ASTM D 1238
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(断裂) MPa psi 50 mm/min; ISO 527
MPa psi Type I, 50 mm/min; ASTM D 638
抗张强度(屈服) MPa psi Type I, 50 mm/min; ASTM D 638
MPa psi 50 mm/min; ISO 527
伸长率 (断裂) 50 mm/min; ISO 527
Type I, 50 mm/min; ASTM D 638
屈服伸长率 50 mm/min; ISO 527
Type I, 50 mm/min; ASTM D 638
拉伸模量 GPa ksi 50 mm/min; ASTM D 638
GPa ksi 1 mm/min; ISO 527
弯曲强度 MPa psi 2 mm/min; ISO 178
MPa psi 1.3 mm/min, 50 mm span; ASTM D 790
弯曲模量 GPa ksi 2 mm/min; ISO 178
GPa ksi 1.3 mm/min, 50 mm span; ASTM D 790
悬壁梁缺口冲击强度 J/cm
@Temperature -30.0 °C
ft-lb/in
@Temperature -22.0 °F
ASTM D 256
J/cm
@Temperature 23.0 °C
ft-lb/in
@Temperature 73.4 °F
ASTM D 256
kJ/m²
@Temperature -30.0 °C
ft-lb/in²
@Temperature -22.0 °F
80*10*3; ISO 180/1A
kJ/m²
@Temperature 23.0 °C
ft-lb/in²
@Temperature 73.4 °F
80*10*3; ISO 180/1A
悬壁梁无缺口冲击强度
@Temperature 23.0 °C
@Temperature 73.4 °F
80*10*3; ISO 180/1U
@Temperature -30.0 °C
@Temperature -22.0 °F
80*10*3; ISO 180/1U
简支梁无缺口冲击强度
@Temperature 23.0 °C
@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
@Temperature -30.0 °C
@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
简支梁缺口冲击强度 J/cm²
@Temperature -30.0 °C
ft-lb/in²
@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
J/cm²
@Temperature 23.0 °C
ft-lb/in²
@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
冲击试验 J
@Temperature 23.0 °C
ft-lb
@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动 µm/m-°C
@Temperature -40.0 - 95.0 °C
µin/in-°F
@Temperature -40.0 - 203 °F
ASTM E 831
µm/m-°C
@Temperature 23.0 - 80.0 °C
µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
线性热膨胀系数,横向流动 µm/m-°C
@Temperature -40.0 - 95.0 °C
µin/in-°F
@Temperature -40.0 - 203 °F
ASTM E 831
µm/m-°C
@Temperature 23.0 - 80.0 °C
µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-2
载荷下热变形温度(1.8 MPa) °C °F Flatw 80*10*4 sp=64mm; ISO 75/Af
°C
@Thickness 3.20 mm
°F
@Thickness 0.126 in
unannealed; ASTM D 648
维卡软化温度 °C °F Rate B/50; ISO 306
°C °F Rate A/50; ASTM D 1525
°C °F Rate B/120; ISO 306
光学性能额定值 (公制)额定值 (英制)测试方法
Transmission, Visible transparent; thickness not quantified