| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 填料含量 | ASTM D229 | ||
| 水分吸收 | 23°C / 50% RH; ISO 62 | ||
| 饱和吸水率 | ISO 62 | ||
| 粘度 | cP | cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| cP | cP | Melt Viscosity, 250°C, 1500 sec-1; ISO 11443 | |
| 线性成型收缩率,Flow | cm/cm | in/in | on Tensile Bar; SABIC Method |
| cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method | |
| 线性成型收缩率，横向 | cm/cm | in/in | on Tensile Bar; SABIC Method |
| 熔体流动速率 | g/10 min @Load 2.16 kg, Temperature 250 °C | g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| g/10 min @Load 2.16 kg, Temperature 250 °C | g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 | |
| Melt Index of Compound | g/10 min @Load 2.16 kg, Temperature 250 °C | g/10 min @Load 4.76 lb, Temperature 482 °F | MVR [cm^3/10 min]; ISO 1133 |
| g/10 min @Load 5.00 kg, Temperature 250 °C | g/10 min @Load 11.0 lb, Temperature 482 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（R 级） | ISO 2039-2 | ||
| 硬度，H358/30 | MPa | psi | ISO 2039-1 |
| 抗张强度(断裂) | MPa | psi | 5 mm/min; ISO 527 |
| MPa | psi | Type I, 5 mm/min; ASTM D638 | |
| 抗张强度(屈服) | MPa | psi | 5 mm/min; ISO 527 |
| MPa | psi | Type I, 5 mm/min; ASTM D638 | |
| 伸长率 (断裂) | Type I, 5 mm/min; ASTM D638 | ||
| 5 mm/min; ISO 527 | |||
| Flexural Strain, break, 2 mm/min; ISO 178 | |||
| 屈服伸长率 | Type I, 5 mm/min; ASTM D638 | ||
| 5 mm/min; ISO 527 | |||
| 拉伸模量 | GPa | ksi | 5 mm/min; ASTM D638 |
| GPa | ksi | 1 mm/min; ISO 527 | |
| 弯曲强度 | MPa | psi | 2 mm/min; ISO 178 |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| MPa | psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| GPa | ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| J/cm @Temperature 0.000 °C | ft-lb/in @Temperature 32.0 °F | ASTM D256 | |
| J/cm @Temperature -30.0 °C | ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | ASTM D4812 |
| J/cm @Temperature -30.0 °C | ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |
| 悬壁梁缺口冲击强度 | kJ/m² | ft-lb/in² | 80*10*4; ISO 180/1A |
| kJ/m² @Temperature 0.000 °C | ft-lb/in² @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | kJ/m² | ft-lb/in² | 80*10*4; ISO 180/1U |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179/2C |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179/2C | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| J/cm² | ft-lb/in² | ISO 179/2C | |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179/2C | |
| 落锤总能量 | J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| ohm-cm | ohm-cm | IEC 60093 | |
| 表面电阻 | >= ohm | >= ohm | ROA; IEC 60093 |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| kV/mm @Thickness 1.50 mm | kV/in @Thickness 0.0591 in | in oil; IEC 60243-1 | |
| kV/mm @Thickness 1.60 mm | kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |
| kV/mm @Thickness 0.800 mm | kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| 相比耐漏电起痕指数(CTI) | V | V | IEC 60112 |
| V | V | UL 746A | |
| 热丝引燃 (HWI) | sec | sec | UL 746A |
| 高电弧燃烧，HAI | >= arcs | >= arcs | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |