| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D792 |
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D570 |
| 水分吸收 | 23°C / 50% RH; ISO 62 | ||
| 饱和吸水率 | ISO 62 | ||
| 线性成型收缩率,Flow | cm/cm | in/in | on Tensile Bar; SABIC Method |
| cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method | |
| 线性成型收缩率，横向 | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | Type I, 50 mm/min; ASTM D638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | MPa | psi | SABIC - Japan Method |
| MPa | psi | Type I, 50 mm/min; ASTM D638 | |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | Type I, 50 mm/min; ASTM D638 | ||
| 50 mm/min; ISO 527 | |||
| SABIC - Japan Method | |||
| 屈服伸长率 | Type I, 50 mm/min; ASTM D638 | ||
| 50 mm/min; ISO 527 | |||
| 拉伸模量 | GPa | ksi | 1 mm/min; ISO 527 |
| GPa | ksi | 5 mm/min; ASTM D638 | |
| 弯曲强度 | MPa | psi | ASTM D790 |
| MPa | psi | 2 mm/min; ISO 178 | |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | GPa | ksi | ASTM D790 |
| GPa | ksi | 2 mm/min; ISO 178 | |
| GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | J/cm | ft-lb/in | ASTM D256 |
| kJ/m² | ft-lb/in² | 80*10*4; ISO 180/1A | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 落锤总能量 | J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | IEC 60093 |
| 表面电阻 | >= ohm | >= ohm | ROA; IEC 60093 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 介电强度 | kV/mm @Thickness 1.60 mm | kV/in @Thickness 0.0630 in | in oil; ASTM D149 |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | V | V | IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature -30.0 - 30.0 °C | µin/in-°F @Temperature -22.0 - 86.0 °F | TMA |
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 维卡软化温度 | °C | °F | Rate B/50; ASTM D1525 |
| °C | °F | Rate B/50; ISO 306 | |
| °C | °F | Rate B/120; ISO 306 | |
| UL RTI | °C | °F | UL 746B |
| UL RTI，机械冲击 | °C | °F | UL 746B |
| UL RTI，机械无冲击 | °C | °F | UL 746B |
| 可燃性(UL94) | @Thickness 0.450 mm | @Thickness 0.0177 in | UL 94 |
| @Thickness 0.800 mm | @Thickness 0.0315 in | UL 94 | |
| 极限氧指数 | ISO 4589 | ||
| 灼热丝试验 | °C | °F | IEC 60695-2-13 |
| °C @Thickness 1.00 mm | °F @Thickness 0.0394 in | IEC 60695-2-12 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASS | IEC 60695-10-2 |