| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | foam molded; ASTM D792 |
| g/cc | g/cc | ASTM D792 | |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D570 |
| 平衡吸湿 | ASTM D570 | ||
| 线性成型收缩率,Flow | cm/cm @Thickness 6.40 mm | in/in @Thickness 0.252 in | SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa @Thickness 6.35 mm | psi @Thickness 0.250 in | ASTM D638 |
| 伸长率 (断裂) | @Thickness 6.35 mm | @Thickness 0.250 in | ASTM D638 |
| 拉伸模量 | GPa @Thickness 6.40 mm | ksi @Thickness 0.252 in | ASTM D638 |
| 弯曲强度 | MPa | psi | 6.4 mm; ASTM D790 |
| 弯曲模量 | GPa | ksi | 6.4 mm; ASTM D790 |
| 悬壁梁无缺口冲击强度 | J/cm | ft-lb/in | ASTM D4812 |
| 落锤总能量 | J | ft-lb | SABIC Method |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | ohm-cm | ohm-cm | ASTM D257 |
| 表面电阻 | >= ohm | >= ohm | ASTM D257 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 |
| @Frequency 100 Hz | @Frequency 100 Hz | ASTM D150 | |
| 耗散因数 | @Frequency 100 Hz | @Frequency 100 Hz | ASTM D150 |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D150 | |
| 耐电弧性 | sec | sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | V | V | UL 746A |
| 高压电弧跟踪率，HVTR | >= mm/min | >= in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 95.0 °C | µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 比热容 | J/g-°C | BTU/lb-°F | ASTM C351 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C177 |
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D648 |
| UL RTI | °C | °F | UL 746B |
| UL RTI，机械冲击 | °C | °F | UL 746B |
| UL RTI，机械无冲击 | °C | °F | UL 746B |
| 可燃性(UL94) | @Thickness 2.99 mm | @Thickness 0.118 in | UL 94 |
| @Thickness 2.99 mm | @Thickness 0.118 in | UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| FOAM - ELECTRICAL 6.4 mm Wt Reduction | 20% | |
| FOAM - Flame Class Minimum Density | 0.85g/cm^3 | |
| FOAM - IMPACT 6.4 mm Wt Reduction | 10% | |
| FOAM - MECHANICAL 6.4 mm Wt Reduction | 10% | |
| FOAM - PHYSICAL 6.4mm Wt Reduction | 10% | |
| FOAM - THERMAL 6.4mm Wt Reduction | 10% |