HOS-Technik Homide 250 Bismaleimide Resin

Homide 250 is a prepolymer bismaleimide resin system with a low softening range of 90-125°C supplied in powder form. The resin can be cured thermally to create a cross-linked thermoset with excellent thermal and mechanical resistance. Homide 250 can be processed in powder form or dissolved in an organic solvent, such as dimethylformamide or N-methylpyrrolidone, up to a concentration of 45% for the production of composite materials.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	g/cc	lb/in³	EN 60893
吸水率			EN 60893

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度	MPa @Thickness >=1.60 mm	psi @Thickness >=0.0630 in	EN 60893
弹性模量	GPa @Thickness >=1.60 mm	ksi @Thickness >=0.0630 in	EN 60893
弯曲强度	MPa @Thickness >=1.60 mm, Temperature 200 °C	psi @Thickness >=0.0630 in, Temperature 392 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=1.60 mm, Temperature 150 °C	psi @Thickness >=0.0630 in, Temperature 302 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=1.60 mm, Temperature 100 °C	psi @Thickness >=0.0630 in, Temperature 212 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=1.60 mm, Temperature 50.0 °C	psi @Thickness >=0.0630 in, Temperature 122 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=1.60 mm, Temperature 20.0 °C	psi @Thickness >=0.0630 in, Temperature 68.0 °F	Perpendicular to laminations; EN 60893
抗压强度	MPa @Thickness >=5.00 mm, Temperature 200 °C	psi @Thickness >=0.197 in, Temperature 392 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=5.00 mm, Temperature 150 °C	psi @Thickness >=0.197 in, Temperature 302 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=5.00 mm, Temperature 100 °C	psi @Thickness >=0.197 in, Temperature 212 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=5.00 mm, Temperature 50.0 °C	psi @Thickness >=0.197 in, Temperature 122 °F	Perpendicular to laminations; EN 60893
	MPa @Thickness >=5.00 mm, Temperature 20.0 °C	psi @Thickness >=0.197 in, Temperature 68.0 °F	Perpendicular to laminations; EN 60893
剪切强度	MPa @Thickness >=5.00 mm	psi @Thickness >=0.197 in	Parallel to laminations; EN 60893
Izod Impact Resistance	J/cm² @Thickness >=127 mm	ft-lb/in² @Thickness >=5.00 in	Parallel to laminations; EN 60893

电气性能	额定值 (公制)	额定值 (英制)	测试方法
绝缘电阻	ohm	ohm	After immersion in water; EN 60893
介电常数	@Thickness >=3.00 mm, Frequency 50.0 Hz	@Thickness >=0.118 in, Frequency 50.0 Hz	EN 60893
介电强度	kV/mm @Thickness >=3.00 mm, Temperature 90.0 °C	kV/in @Thickness >=0.118 in, Temperature 194 °F	Tested in oil. Perpendicular to laminations.; EN 60893
耗散因数	@Thickness >=3.00 mm, Frequency 50.0 Hz	@Thickness >=0.118 in, Frequency 50.0 Hz	EN 60893

热性能	额定值 (公制)	额定值 (英制)	测试方法
可燃性(UL94)	@Thickness 3.00 mm	@Thickness 0.118 in	EN 60893