Capron 8362 HS is generally recommended for applications such as wheel covers and hubs, mirror housings, appliance components and power tool housings.
Data provided by Allied Signal.
Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.
Melt Temperature: 270-300 degC (518-572 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.
Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Melt Density |
| g/cc | lb/in³ | ISO data | |
| 平衡吸湿 | 50% RH; 23°C; ISO data | ||
| 饱和吸水率 | in water; 23°C; ISO data | ||
| 线性成型收缩率 | cm/cm | in/in | ASTM Data MD |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | ASTM value at 50 mm/min. |
| MPa | psi | ISO value at 50 mm/min. | |
| 伸长率 (断裂) | Nominal | ||
| Nominal | |||
| 弯曲强度 | MPa | psi | ASTM Data |
| 弯曲模量 | GPa | ksi | ISO Value |
| GPa | ksi | ASTM Value | |
| 泊松比 | ISO data |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比热容 | J/g-°C | BTU/lb-°F | Melt value |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | Melt |
| 熔融温度 | °C | °F | ASTM and ISO test |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ASTM Data |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 干燥温度 | °C | °F | See Materials Notes |