Key characteristics:
Information provided by NILIT.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM D792, ISO 1183 |
| 吸水率 | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 | ||
| 饱和吸水率 | sim. ISO 62 | ||
| 线性成型收缩率,Flow | cm/cm | in/in | Euronil |
| 线性成型收缩率，横向 | cm/cm | in/in | Euronil |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | MPa | psi | ISO 527, ASTM D638 |
| 伸长率 (断裂) | ISO 527, ASTM D638 | ||
| 拉伸模量 | GPa | ksi | ISO 527, ASTM D638 |
| 弯曲强度 | MPa | psi | ISO 178, ASTM D790 |
| MPa @Temperature 90.0 °C | psi @Temperature 194 °F | ISO 178, ASTM D790 | |
| 弯曲模量 | GPa | ksi | ISO 178, ASTM D790 |
| GPa @Temperature 90.0 °C | ksi @Temperature 194 °F | ISO 178, ASTM D790 | |
| 悬壁梁缺口冲击强度 | kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 180/1A |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |
| 简支梁无缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179 |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179 | |
| 简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179 |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电强度 | kV/mm @Thickness 2.00 mm | kV/in @Thickness 0.0787 in | ASTM D149 |
| Comparative Tracking Index | V @Thickness 3.20 mm | V @Thickness 0.126 in | Sol. B; IEC 112, UL 746A |
| V @Thickness 3.20 mm | V @Thickness 0.126 in | Sol. A; IEC 112, UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 最高工作温度, Air | °C | °F | 20,000 hr; IEC 216 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | ISO 75, ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75, ASTM D648 |
| 维卡软化温度 | °C | °F | 49 N; ISO 306, ASTM D1525 |
| °C | °F | 9.8 N; ISO 306, ASTM D1525 | |
| 可燃性(UL94) | @Thickness 0.800 mm | @Thickness 0.0315 in | |
| @Thickness 1.60 mm | @Thickness 0.0630 in | ||
| @Thickness 3.20 mm | @Thickness 0.126 in | ||
| 极限氧指数 | ASTM D2863 | ||
| 灼热丝易燃指数 | °C @Thickness 3.20 mm | °F @Thickness 0.126 in | Glow Wire Flammability Index; IEC 694-2-12 |
| °C @Thickness 0.800 mm | °F @Thickness 0.0315 in | Glow Wire Flammability Index; IEC 694-2-12 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 射嘴温度 | °C | °F | |
| 1区 | °C | °F | hopper |
| 2区 | °C | °F | |
| 3区 | °C | °F | |
| 4区 | °C | °F | |
| 加工（熔体）温度 | °C | °F | Do not melt above 300°C |
| 模具温度 | °C | °F | Preferred |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 注射压力 | MPa | psi |
| 材料描述 | 测试方法 | |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | B28 | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 Mpa |