| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D 792 |
| 密度 | g/cc | lb/in³ | ASTM D 792 |
| g/cc | lb/in³ | ISO 1183 | |
| 吸水率 | @Time 86400 sec | @Time 24.0 hour | ASTM D 570 |
| 平衡吸湿 | 23°C / 50% RH; ISO 62 | ||
| @Temperature 23.0 °C | @Temperature 73.4 °F | ASTM D 570 | |
| @Temperature 100 °C | @Temperature 212 °F | ASTM D 570 | |
| 饱和吸水率 | @Temperature 23.0 °C | @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | ASTM D 785 | ||
| 洛氏硬度（R 级） | ASTM D 785 | ||
| 抗张强度(断裂) | MPa | psi | 50 mm/min; ISO 527 |
| MPa | psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D 638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D 638 | |||
| 屈服伸长率 | 50 mm/min; ISO 527 | ||
| Type I, 50 mm/min; ASTM D 638 | |||
| 拉伸模量 | GPa | ksi | 1 mm/min; ISO 527 |
| GPa | ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | MPa | psi | 2 mm/min; ISO 178 |
| MPa | psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| GPa | ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 悬壁梁无缺口冲击强度 | J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A | |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| @Temperature -30.0 °C | @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | @Temperature 23.0 °C | @Temperature 73.4 °F | 80*10*3; ISO 180/1U |
| @Temperature -30.0 °C | @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | @Temperature 23.0 °C | @Temperature 73.4 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| @Temperature -30.0 °C | @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ISO 179/2C | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 拉伸冲击强度 | kJ/m² | ft-lb/in² | Type S; ASTM D 1822 |
| 落锤总能量 | J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | ASTM D 3029 |
| 冲击试验 | J @Temperature 23.0 °C | ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= ohm-cm | >= ohm-cm | ASTM D 257 |
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D 150 | |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D 150 | |
| 介电强度 | kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in air; ASTM D 149 |
| kV/mm @Thickness 3.20 mm | kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | |
| 耗散因数 | @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | ASTM D 150 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 | |
| @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | ASTM D 150 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| µm/m-°C @Temperature -40.0 - 40.0 °C | µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 比热容 | J/g-°C | BTU/lb-°F | ASTM C 351 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C 177 |
| W/m-K | BTU-in/hr-ft²-°F | ISO 8302 | |
| 载荷下热变形温度(0.46 MPa) | °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D 648 |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| °C @Thickness 6.40 mm | °F @Thickness 0.252 in | unannealed; ASTM D 648 | |
| 维卡软化温度 | °C | °F | Rate B/50; ASTM D 1525 |
| °C | °F | Rate B/50; ISO 306 | |
| °C | °F | Rate B/120; ISO 306 | |
| UL RTI | °C | °F | UL 746B |
| UL RTI，机械冲击 | °C | °F | UL 746B |
| UL RTI，机械无冲击 | °C | °F | UL 746B |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | ASTM D 542 | ||
| 雾度 | @Thickness 2.54 mm | @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | @Thickness 2.54 mm | @Thickness 0.100 in | ASTM D 1003 |