| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | g/cc | g/cc | ASTM D 792 |
| 密度 | g/cc | lb/in³ | ISO 1183 |
| 线性成型收缩率,Flow | cm/cm @Thickness 3.20 mm | in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| g/10 min @Load 1.20 kg, Temperature 300 °C | g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hardness, Rockwell L | ASTM D 785 | ||
| 洛氏硬度（R 级） | ASTM D 785 | ||
| 抗张强度(断裂) | MPa | psi | Type I, 50 mm/min; ASTM D 638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | MPa | psi | Type I, 50 mm/min; ASTM D 638 |
| MPa | psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | Type I, 50 mm/min; ASTM D 638 | ||
| 50 mm/min; ISO 527 | |||
| 屈服伸长率 | Type I, 50 mm/min; ASTM D 638 | ||
| 50 mm/min; ISO 527 | |||
| 拉伸模量 | GPa | ksi | 1 mm/min; ISO 527 |
| GPa | ksi | 5 mm/min; ASTM D 638 | |
| 弯曲强度 | MPa | psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| MPa | psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | GPa | ksi | 2 mm/min; ISO 178 |
| GPa | ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | J/cm @Temperature -30.0 °C | ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| J/cm @Temperature 23.0 °C | ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 简支梁缺口冲击强度 | J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | J | ft-lb | Multiaxial Impact; ISO 6603 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 | |
| @Frequency 1000 Hz | @Frequency 1000 Hz | IEC 60250 | |
| 介电强度 | kV/mm @Thickness 1.60 mm | kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 |
| kV/mm @Thickness 0.800 mm | kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IEC 60250 |
| @Frequency 1000 Hz | @Frequency 1000 Hz | IEC 60250 | |
| @Frequency 50.0 - 60.0 Hz | @Frequency 50.0 - 60.0 Hz | IEC 60250 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hot Ball Pressure Test | <= °C | <= °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | °C | °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | °C | °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| °C @Thickness 3.20 mm | °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 维卡软化温度 | °C | °F | Rate B/50; ASTM D 1525 |
| °C | °F | Rate B/50; ISO 306 | |
| °C | °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in | UL 94 |
| @Thickness 3.00 mm | @Thickness 0.118 in | 2nd value; UL 94 | |
| 灼热丝易燃指数 | °C @Thickness 1.50 mm | °F @Thickness 0.0591 in | Glow Wire Flammability Index; IEC 60695-2-12 |
| °C @Thickness 3.00 mm | °F @Thickness 0.118 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | pass | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | F | ASTM D 3363 |