Corrosion: Although all Coors Ceramics are highly resistant to chemical attack, Coors recommends obtaining specific application data from Coors before design finalization.
Data Provided by the manufacturer, Coors Ceramics Co.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | ASTM C20 |
| 吸水率 | ASTM C373 | ||
| 粒径 | µm | µm | Average Crystal Size - Thin Section Test |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Knoop Microhardness | 1000 g load | ||
| Hardness, Rockwell 45 N | GPa | ||
| 极限抗拉强度 | MPa | psi | ACMA Test #4 |
| 弹性模量 | GPa | ksi | ASTM C848 |
| 弯曲强度 | MPa | psi | ASTM F417 |
| 抗压强度 | MPa | psi | ASTM C773 |
| 泊松比 | ASTM C848 | ||
| Fracture Toughness | MPa-m½ | ksi-in½ | Notched Beam |
| 剪切模量 | GPa | ksi | Calculated |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | >= ohm-cm | >= ohm-cm | ASTM D1829 |
| ohm-cm @Temperature 1000 °C | ohm-cm @Temperature 1830 °F | ASTM D1829 | |
| ohm-cm @Temperature 500 °C | ohm-cm @Temperature 932 °F | ASTM D1829 | |
| 介电常数 | @Frequency 1e+6 Hz | @Frequency 1e+6 Hz | |
| 介电强度 | kV/mm | kV/in | ac; ASTM D116 |
| 介电损耗指数 | at 25°C, 1 MHz; ASTM D2520 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C @Temperature 25.0 - 1000 °C | µin/in-°F @Temperature 77.0 - 1830 °F | ASTM C372 |
| 比热容 | J/g-°C | BTU/lb-°F | ASTM E1269 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM C408 |
| 最高工作温度, Air | °C | °F | No Load |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | White |