SABIC® PP FPH50

SABIC® PP FPH50 is a grade developed for thin wall packaging as well as the caps & closures market. The grade is nucleated and is characterised by a high crystallisation temperature, excellent flow behaviour in combination with a high stiffness. SABIC® PP FPH50 allows for very cost efficient processing on the basis of easy mould filling, very short cycle times and robust processing behaviour in combination with pigments. It has a very good antistatic performance and shows easy demoulding.

SABIC® PP FPH50 is typically used in thin wall packing applications both for food and non-food segments. In caps and closure, the grade could be used for wide mouth caps, amongst others. In media packaging, the grade offers opportunities for cycle time optimisation. The grade has excellent heat deflection temperature making it particularly suitable for hot fill applications.

This product is not intended for and must not be used in any pharmaceutical/medical applications.

基本信息
黄卡编号	E111275-100605366
添加剂	成核剂 抗静电性
特性	成核的 刚性，高 均聚物 抗静电性 快的成型周期 良好的流动性 脱模性能良好
用途	包装 薄壁包装 护罩 媒介包装 食品包装 外壳
UL文件号	E111275
加工方法	注射成型

物理性能	额定值	单位制	测试方法
比重		g/cm³	ASTM D792, ISO 1183
熔流率（熔体流动速率） (230°C/2.16 kg)		g/10 min	ASTM D1238, ISO 1133

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级)			ASTM D785
肖氏硬度 (邵氏 D)			ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量
1% 正割 1		MPa	ASTM D638
--		MPa	ISO 527-2/1A/1
抗张强度
屈服 2		MPa	ASTM D638
屈服		MPa	ISO 527-2/1A/50
伸长率
屈服 3		%	ASTM D638
屈服		%	ISO 527-2/1A/50

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度 (23°C)		kJ/m²	ISO 179/1eA
悬壁梁缺口冲击强度
23°C		J/m	ASTM D256A
23°C		kJ/m²	ISO 180/1A

热性能	额定值	单位制	测试方法
载荷下热变形温度
0.45 MPa, 未退火		°C	ASTM D648
0.45 MPa, 未退火 4		°C	ISO 75-2/Bf
1.8 MPa, 未退火		°C	ASTM D648
1.8 MPa, 未退火 5		°C	ISO 75-2/Af
维卡软化温度
--		°C	ASTM D1525, ISO 306/A120 6 6
--		°C	ASTM D1525, ISO 306/B120 7 7

备注
1 .	1.0 mm/min
2 .	50 mm/min
3 .	50 mm/min
4 .	testbar 80*10*4mm
5 .	testbar 80*10*4mm
6 .	标准 B (120°C/h), 压 力1 (10N)
7 .	标准 B (120°C/h), 载荷2 (50N)