CERTENE™ LDF-0822A

LDF-0822A is a certified prime resin specially designed for production of shrink wrapping Blown films for case bundling applications requiring excellent shrink performance, very high toughness, good puncture and burn-through resistance. LDF-0822A is also recommended for impact liner films. It features easy processability with excellent film optical and mechanical properties. Minimum recommended film thickness is 1.5 mils. LDF-0822A contains no slip and no antiblock.

基本信息
特性	超高韧性 低密度 光学性能 抗穿孔性 可加工性，良好 收缩性高
用途	薄膜 衬里 收缩性薄膜
形式	粒子
加工方法	吹塑薄膜

物理性能	额定值	单位制	测试方法
密度		g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)		g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试		µm
割线模量			ASTM D882
1% 正割, MD : 38 µm		MPa	ASTM D882
1% 正割, TD : 38 µm		MPa	ASTM D882
抗张强度			ASTM D882
MD : 屈服, 38 µm		MPa	ASTM D882
TD : 屈服, 38 µm		MPa	ASTM D882
MD : 断裂, 38 µm		MPa	ASTM D882
TD : 断裂, 38 µm		MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 µm		%	ASTM D882
TD : 断裂, 38 µm		%	ASTM D882
落锤冲击 (38 µm)		g	ASTM D1709A
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 µm		g	ASTM D1922
TD : 38 µm		g	ASTM D1922

光学性能	额定值	单位制	测试方法
光泽度 (45°, 38.1 µm)			ASTM D2457
雾度 (38.1 µm)		%	ASTM D1003

补充信息
This Specimen was compression molded and was tested according to ASTM D1928 Procedure C.

挤出	额定值	单位制
熔体温度		°C