Modified homopolymer PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc conte nt. Decreased shrinkage. General application in all industry branches. Delivered in natural mode and in the full RAL colour scale.
Packaging, transport, stocking
The product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.
Information Provided by Plastcom spol. s r.o.| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | |
| 线性成型收缩率 | cm/cm | in/in | |
| 线性成型收缩率，横向 | cm/cm | in/in | |
| 熔体流动速率 | g/10 min @Load 0.325 kg, Temperature 270 °C | g/10 min @Load 0.716 lb, Temperature 518 °F |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | MPa | psi | |
| 伸长率 (断裂) | |||
| 拉伸模量 | GPa | ksi | |
| 弯曲强度 | MPa | psi | |
| 弯曲模量 | GPa | ksi | |
| 简支梁无缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | ||
| 简支梁缺口冲击强度 | J/cm² @Temperature -20.0 °C | ft-lb/in² @Temperature -4.00 °F | |
| J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(1.8 MPa) | °C | °F | |
| 维卡软化温度 | °C | °F | B |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | °C | °F | |
| 模具温度 | °C | °F | |
| 干燥温度 | °C | °F | |
| 干燥时间 | hour | hour | |
| 注射压力 | MPa | psi |