The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O) and carbon-carbon (-C-C- bond) comonomer groups are incorporated into its main chain. Therefore the copolymer has superior chemical and thermal stability, compared with acetal homopolymer.
Acetal co-polymer is well-balanced in terms of mechanical, chemical and thermal properties, and its superior moldability allows it to be widely employed in various industrial fields.
Information provided by PolyPlastics.
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | g/cc | lb/in³ | ISO 1183 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
极限抗拉强度 | MPa | psi | ISO 527-1, 2 |
伸长率 (断裂) | ISO 527-1, 2 | ||
拉伸模量 | GPa | ksi | ISO 527-1, 2 |
弯曲强度 | MPa | psi | ISO 178 |
弯曲模量 | GPa | ksi | ISO 178 |
简支梁缺口冲击强度 | J/cm² | ft-lb/in² | ISO 179/1eA |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | ohm-cm | ohm-cm | IEC 60093 |
表面电阻 | ohm | ohm | IEC 60093 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线性热膨胀系数 | µm/m-°C @Temperature 23.0 - 55.0 °C | µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-2 |
线性热膨胀系数,横向流动 | µm/m-°C @Temperature 23.0 - 55.0 °C | µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-2 |
载荷下热变形温度(1.8 MPa) | °C | °F | ISO 75-1, 2 |
可燃性(UL94) |