Industry Specifications: USA Aerospace: AMS 4974.
Features: TIMETAL 679 has excellent tensile strength and is creep resistant up to 450°C. It is a three-phase alloy at room temperature, having an alpha + beta + compound field and a maximum temperature of 925°C is recommended. It is nonmagnetic.
Typical heat treatment for this alloy: Solution heat treatment: 900°C for 30 min, air cool. Aging heat treatment: 500°C for 24 hrs, air cool.
Data provided by TIMET.
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | g/cc | lb/in³ | Typical |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
极限抗拉强度 | >= MPa | >= psi | |
抗张强度(屈服) | >= MPa @Strain 0.200 % | >= psi @Strain 0.200 % | |
伸长率 (断裂) | |||
面积减少 | |||
弹性模量 | GPa | ksi | Typical |
Fatigue Strength | MPa | psi | Limit; test specifics not reported |
剪切模量 | GPa | ksi |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
电阻率 | ohm-cm | ohm-cm |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线性热膨胀系数 | µm/m-°C @Temperature 20.0 °C | µin/in-°F @Temperature 68.0 °F | |
导热系数 | W/m-K | BTU-in/hr-ft²-°F | |
Beta Transus | °C | °F |
构成要素属性 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
铝 | |||
Hydrogen, H | |||
铁 | |||
钼 | |||
Oxygen, O | |||
硅酮 | |||
锡 | |||
钛 | Calculated as remainder | ||
Zirconium, Zr |