Applications:
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | g/cc | lb/in³ | ISO 1183/B |
表观密度 | g/cc | lb/in³ | ISO 60 |
线性成型收缩率,Flow | cm/cm | in/in | ISO 294-4 |
熔体流动速率 | g/10 min @Load 10.0 kg, Temperature 220 °C | g/10 min @Load 22.0 lb, Temperature 428 °F | ISO 60 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(屈服) | MPa @Thickness 3.20 mm | psi @Thickness 0.126 in | Injection Molded; ISO 527-2/50 |
MPa @Thickness 3.20 mm | psi @Thickness 0.126 in | Injection Molded; ISO 527-2/100 | |
Elongation at Yield | @Thickness 3.20 mm | @Thickness 0.126 in | Injection Molded; ISO 527-2/50 |
@Thickness 3.20 mm | @Thickness 0.126 in | Injection Molded; ISO 527-2/100 | |
拉伸模量 | GPa @Thickness 3.20 mm | ksi @Thickness 0.126 in | Injection Molded; ISO 527-2 |
弯曲强度 | MPa @Thickness 3.20 mm | psi @Thickness 0.126 in | 3-points, 2 mm/min, Injection Molded; ISO 178 |
弯曲模量 | GPa @Thickness 3.20 mm | ksi @Thickness 0.126 in | 3-points, 2 mm/min, Injection Molded; ISO 178 |
悬壁梁缺口冲击强度 | kJ/m² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | Injection Molded; ISO 180/A |
kJ/m² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Injection Molded; ISO 180/A | |
简支梁缺口冲击强度 | J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | Injection Molded; ISO 179/2 |
J/cm² @Temperature -30.0 °C | ft-lb/in² @Temperature -22.0 °F | Injection Molded; ISO 179/1eA | |
J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Injection Molded; ISO 179/2 | |
J/cm² @Temperature 23.0 °C | ft-lb/in² @Temperature 73.4 °F | Injection Molded; ISO 179/1eA |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
载荷下热变形温度(1.8 MPa) | °C | °F | Annealed; ISO 75-2/A |
维卡软化温度 | °C | °F | ISO 306/B50 |
可燃性(UL94) | @Thickness 1.50 mm | @Thickness 0.0591 in | |
@Thickness 3.00 mm | @Thickness 0.118 in | ||
Flame Spread | mm/min | in/min | ISO 3795 |
材料描述 | 测试方法 | |
---|---|---|
Carbon Emission | 200 µg/g | VDA 277 |