物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
密度 | g/cc | lb/in³ |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
Hardness, Brinell | @Thickness 7.90 - 25.0 mm | @Thickness 0.311 - 0.984 in | |
@Thickness 60.0 - 150 mm | @Thickness 2.36 - 5.91 in | ||
@Thickness 25.0 - 60.0 mm | @Thickness 0.984 - 2.36 in | ||
抗张强度 | >= MPa @Thickness 100 - 140 mm | >= psi @Thickness 3.94 - 5.51 in | Temper T651; Standard EN 485-2 |
>= MPa @Thickness 7.90 - 12.5 mm | >= psi @Thickness 0.311 - 0.492 in | Temper T651; Standard EN 485-2 | |
>= MPa @Thickness 12.5 - 40.0 mm | >= psi @Thickness 0.492 - 1.57 in | Temper T651; Standard EN 485-2 | |
>= MPa @Thickness 40.0 - 80.0 mm | >= psi @Thickness 1.57 - 3.15 in | Temper T651; Standard EN 485-2 | |
>= MPa @Thickness 80.0 - 100 mm | >= psi @Thickness 3.15 - 3.94 in | Temper T651; Standard EN 485-2 | |
MPa @Thickness 60.0 - 150 mm | psi @Thickness 2.36 - 5.91 in | Typical Strength | |
MPa @Thickness 7.90 - 25.0 mm | psi @Thickness 0.311 - 0.984 in | Typical Strength | |
MPa @Thickness 25.0 - 60.0 mm | psi @Thickness 0.984 - 2.36 in | Typical Strength | |
抗张强度(屈服) | >= MPa @Strain 0.200 %, Thickness 7.90 - 12.5 mm | >= psi @Strain 0.200 %, Thickness 0.311 - 0.492 in | Temper T651; Standard EN 485-2 |
>= MPa @Strain 0.200 %, Thickness 12.5 - 40.0 mm | >= psi @Strain 0.200 %, Thickness 0.492 - 1.57 in | Temper T651; Standard EN 485-2 | |
>= MPa @Strain 0.200 %, Thickness 40.0 - 80.0 mm | >= psi @Strain 0.200 %, Thickness 1.57 - 3.15 in | Temper T651; Standard EN 485-2 | |
>= MPa @Strain 0.200 %, Thickness 80.0 - 100 mm | >= psi @Strain 0.200 %, Thickness 3.15 - 3.94 in | Temper T651; Standard EN 485-2 | |
>= MPa @Strain 0.200 %, Thickness 100 - 140 mm | >= psi @Strain 0.200 %, Thickness 3.94 - 5.51 in | Temper T651; Standard EN 485-2 | |
MPa @Strain 0.200 %, Thickness 60.0 - 150 mm | psi @Strain 0.200 %, Thickness 2.36 - 5.91 in | Typical Strength | |
MPa @Strain 0.200 %, Thickness 7.90 - 25.0 mm | psi @Strain 0.200 %, Thickness 0.311 - 0.984 in | Typical Strength | |
MPa @Strain 0.200 %, Thickness 25.0 - 60.0 mm | psi @Strain 0.200 %, Thickness 0.984 - 2.36 in | Typical Strength | |
伸长率 (断裂) | @Thickness 80.0 - 100 mm | @Thickness 3.15 - 3.94 in | Temper T651; Standard EN 485-2 |
@Thickness 100 - 140 mm | @Thickness 3.94 - 5.51 in | Temper T651; Standard EN 485-2 | |
@Thickness 40.0 - 80.0 mm | @Thickness 1.57 - 3.15 in | Temper T651; Standard EN 485-2 | |
@Thickness 12.5 - 40.0 mm | @Thickness 0.492 - 1.57 in | Temper T651; Standard EN 485-2 | |
@Thickness 7.90 - 12.5 mm | @Thickness 0.311 - 0.492 in | Temper T651; Standard EN 485-2 | |
@Thickness 60.0 - 150 mm | @Thickness 2.36 - 5.91 in | Typical Elongation | |
@Thickness 7.90 - 25.0 mm | @Thickness 0.311 - 0.984 in | Typical Elongation | |
@Thickness 25.0 - 60.0 mm | @Thickness 0.984 - 2.36 in | Typical Elongation | |
弹性模量 | GPa | ksi |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
电阻率 | ohm-cm | ohm-cm | Temper T651 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线性热膨胀系数 | µm/m-°C @Temperature 20.0 - 100 °C | µin/in-°F @Temperature 68.0 - 212 °F | |
导热系数 | W/m-K | BTU-in/hr-ft²-°F | Temper T651 |
构成要素属性 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
铝 | as balance | ||
铬 | |||
铜 | |||
铁 | |||
Magnesium, Mg | |||
锰 | |||
硅酮 | |||
锌 |