A. Schulman POLYAXIS® PD2000 Polypropylene

Polymer,Thermoplastic,Polypropylene (PP),Polypropylene, Molded

A. Schulman, Inc.

PDF物性文档下载

产品说明:

Description

Polyaxis PD 2000 is a polypropylene specifically designed from rotational molding.

NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR tests were performed on compression molded samples.

Information provided by A. Schulman.

A. Schulman POLYAXIS® PD2000 Polypropylene 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
比重 g/cc g/cc ASTM D792
ESCR 100% Igepal®>= hour >= hour ASTM D1693
化合物熔体指数 g/10 min g/10 min 2.16/230; ASTM D1238
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服) MPa psi 2"/min; ASTM D638
伸长率 (断裂) 2"/min; ASTM D638
弯曲模量 GPa ksi at 1% secant modulus; ASTM D790
冲击试验 J
@Thickness 3.17 mm, Temperature 23.0 °C
ft-lb
@Thickness 0.125 in, Temperature 73.4 °F
ARM impact
热性能额定值 (公制)额定值 (英制)测试方法
载荷下热变形温度(0.46 MPa) °C °F ASTM D648