KPOL-HDPE HD K-10.0/948

High Density Polyethylene Extra high molecular weight, hexene copolymer Extrusion-Blow Molding

Characteristics

• The KPOL HD K-10.0/948, is a high molecular weight high-density polyethylene, copolymer.

• Offers good processability, outstanding stress cracking resistance (ESCR), excellent stiffness and impact strength. Suitable for blow molding of large volumes.

Applications

• Typical blow molded applications include containers and drums from 20 to 200 liters, for chemical, agrochemical and food package, small tanks and bedliner, Pallets, Automotive dunnage, Truck bedliners.

• The KPOL® resin meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

基本信息
添加剂	抗氧化性
特性	刚性，高 高 ESCR（抗应力开裂） 高分子量 高密度 共聚物 抗氧化性 抗撞击性，良好 可加工性，良好 食品接触的合规性
用途	Pallets 包装 鼓 农业应用 汽车领域的应用 容器 食品包装
机构评级	FDA 21 CFR 177.1520(c)
加工方法	吹塑成型 挤出

物理性能	额定值	单位制	测试方法
密度		g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/21.6 kg)		g/10 min	ASTM D1238
抗环境应力开裂
50°C, 1.91 mm, 10% Igepal CO-630		hr	ASTM D1693B
50°C, 3.18 mm, 100% Igepal CO-630		hr	ASTM D1693A

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)			ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度 (屈服)		MPa	ASTM D638
伸长率 (断裂)		%	ASTM D638
弯曲模量 - 正切		MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
拉伸冲击强度		kJ/m²	ASTM D1822

热性能	额定值	单位制	测试方法
脆化温度		°C	ASTM D746
维卡软化温度		°C	ASTM D1525
熔融温度		°C	DSC
Heat Deflection Temperature		°C	ASTM D648