Omnix® 4050物性表-搜物性

基本信息
特性	尺寸稳定性良好刚性，高高强度抗撞击性，良好可喷涂的快的成型周期流动性高热水可成型性优良外观
用途	电气/电子应用领域机械保养/维修汽车电子
RoHS 合规性	RoHS 合规
外观	黑色自然色
形式	粒子
加工方法	水温模具注塑成型注射成型
部件标识代码 (ISO 11469)	>(PA+PPA)-GF50

物理性能	单位制	测试方法
比重	g/cm³	ASTM D792
收缩率 ¹		ISO 294-4
垂直流动方向	%	ISO 294-4
流动方向	%	ISO 294-4

机械性能	单位制	测试方法
拉伸模量	MPa	ISO 527-2
拉伸应力 (屈服)	MPa	ISO 527-2
拉伸应变 (断裂)	%	ISO 527-2
弯曲模量	MPa	ISO 178
弯曲应力	MPa	ISO 178

冲击性能	干燥	调节后的	单位制	测试方法
悬壁梁缺口冲击强度			kJ/m²	ISO 180/A
无缺口伊佐德冲击强度			kJ/m²	ISO 180

热性能	干燥	调节后的	单位制	测试方法
熔融温度			°C	ISO 11357-3

可燃性	干燥	调节后的		测试方法
UL 阻燃等级 (0.800 mm)				UL 94

补充信息
干燥 Typical values shown tested on Dry as Molded samples. Standard Packaging and Labeling: Omnix® 4050 resin is packaged in foil lined, multiwall paper bags containing 25 kg (55 pounds) of material. Individual packages will be plainly marked with the product number, the color, the lot number, and the net weight.

注射	干燥	单位制
干燥温度		°C
干燥时间		hr
料筒后部温度		°C
料筒前部温度		°C
加工（熔体）温度		°C
模具温度		°C

注射说明
Drying: Omnix® 4050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® 4050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

注射说明

Drying: Omnix® 4050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® 4050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

备注
1 .	Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information.

Omnix® 4050

HPPA

Solvay Specialty Polymers

产品说明