Ebalta BLH Epoxy 200 / K 25

Slight discoleration of the hardener by oxygen possible. Discoleration to red-brown of hardener K 25 by oxygen, which doesn't affect the products quality.

Demoulding of laminates made at room temperature (20°C) is possible. The parts show very good strength. To achieve maximum property values for example for flexural strength and heat resistance, we recommend thermal treatment at the recommended temperature.

Applications

• Boatbuilding

• Hand laminating

Properties

• good curing at room temperature

• excellent soaking of aramid fibre cloth

• excellent soaking of glass fibre cloth

• excellent soaking of carbon fibre cloth

• low viscosity

• certified according to "Germanischer Lloyd"

基本信息
特性	低粘度 良好的强度
用途	层压板
外观	绿色

物理性能	额定值	单位制	测试方法
吸水率			DIN 53495
23°C, 24 hr		%	DIN 53495
饱和, 23°C 1		%	DIN 53495

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)			ISO 7619

机械性能	额定值	单位制	测试方法
拉伸模量		MPa	ISO 527-2
拉伸应力		MPa	ISO 527-2
拉伸应变 (断裂)		%	ISO 527-2
弯曲模量		MPa	ISO 178
弯曲应力		MPa	ISO 178

热性能	额定值	单位制	测试方法
热变形温度 (1.8 MPa, 未退火)		°C	ISO 75-2/A
玻璃转化温度		°C	TMA

热固性	额定值	单位制
热固组件
树脂
硬化法
后固化时间 (80°C)		hr

Uncured Properties	额定值	单位制
密度 (20°C)		g/cm³
粘度 (25°C)		Pa·s
固化时间 (20°C)		hr
储存稳定性
20°C 2		min
20°C 3		min

备注
1 .	168 h
2 .	200 g
3 .	100 g